TPU hot melt film
It is a TPU hot melt adhesive film coated on glassine double silicon release paper. Laminating of PVC, leather, cloth and other materials that need to be used at a lower temperature 1.good lamination strength: when applied at textile, the product will have a good bonding performance. 2.good water... -
PES HOT MELT ADHESIVE FILM
It is a PES based on hot melt glue for excellent adhesion. It is an environmentally friendly hot melt adhesive film with thermoplastic polyester as the main body. It is mainly used for bonding various textile fabrics, PVC, ABS, PET, various plastics, leather and various artificial leather, mesh c... -
TPU hot melt film
It is a TPU hot melt adhesive film coated on glassine double silicon release paper. textile fabric,cotton fabric，seamless underwear, seamless pockets, waterproof zippers, waterproof strips, multifunctional clothing, reflective materials and other fields. The compound processing of various elasti... -
TPU hot melt film
It is a TPU hot melt adhesive film which is suitable for the bonding of kinds of materials ,especially bonding of microfiber, leather, cotton, glass fiber board, etc. Compared with liquid glue bonding, this product behaves well on many aspects such as evironment relationship, application process ... -
TPU hot melt film
It is a TPU hot melt adhesive film which is suitable for the bonding of kinds of materials ,especially bonding of material which has high water-resistance requirement. Compared with liquid glue bonding, this product behaves well on many aspects such as evironment relationship, application proces... -
TPU WEB HOT MELT ADHESIVE FILM
Flat pressing Temperature: 120-150 Pressure: 0.2-0.6Mpa Time: 6-10s Complex machine Temperature: 130-170℃ Roller speed: 5-10m/min It is a product without added fluorescent whitening agent. Mainly used in the bonding of various textile fabrics, PVC, ABS, PET, various plastics, leather and various ... -
EVA HOT MELT ADHESIVE FILM
1)Flat press machine Temperature: 150-170℃ Pressure: 0.4-0.6MPa Time: 8-10s 2)Complex machine Temperature: 160-180℃ Pressure: 0.4-0.6MPa Roll speed: 5-6 m/min L043 is suitable for lamination of microfiber and EVA chips, fabrics, paper, etc. 1.good lamination strength: when applied at textile, the... -
H&H Profile-8.11
Flat pressing Temperature: 120-150 Pressure: 0.2-0.6Mpa Time: 6-10s Complex machine Temperature: 130-170℃ Roller speed: 5-10m/min It is a product without added fluorescent whitening agent. Mainly used in the bonding of various textile fabrics, PVC, ABS, PET, various plastics, leather and various... -
PA HOT MELT ADHESIVE FILM
Bonding fabrics, non-woven fabrics, embroidered badges, trademark adhesives,etc. 1.good lamination strength: when applied at textile, the product will have a good bonding performance. 2.Non-toxic and environmental-friendly: It will not give off unpleasant smell and will not have bad influences on... -
PO HOT MELT ADHESIVE FILM
bonding metal materials, coating materials, fabrics, wood, aluminized films,aluminum honeycombs, etc. 1.good lamination strength: when applied at textile, the product will have a good bonding performance. 2.Non-toxic and environmental-friendly: It will not give off unpleasant smell and will not h... -
Thermoplastic polyester film
Bonding of PVC, artificial leather, cloth, fiber and other materials that require lower temperature processing. 1.good lamination strength: when applied at textile, the product will have a good bonding performance. 2.Non-toxic and environmental-friendly: It will not give off unpleasant smell and ... -
PA HOT MELT ADHESIVE FILM
Laminating of various textiles such as fabrics, non-woven fabrics, embroidered badges, trademark adhesives, etc. 1.good lamination strength: when applied at textile, the product will have a good bonding performance. 2.Non-toxic and environmental-friendly: It will not give off unpleasant smell and...