Ordinary Discount H&H Printing - EVA HOT MELT ADHESIVE FILM – HH
Ordinary Discount H&H Printing - EVA HOT MELT ADHESIVE FILM – HH Detail:
1)Flat press machine
Temperature: 150-170℃
Pressure: 0.4-0.6MPa
Time: 8-10s
2)Complex machine
Temperature: 160-180℃
Pressure: 0.4-0.6MPa
Roll speed: 5-6 m/min
L043 is suitable for lamination of microfiber and EVA chips, fabrics, paper, etc.
1.good lamination strength: when applied at textile, the product will have a good bonding performance.
2.Non-toxic and environmental-friendly: It will not give off unpleasant smell and will not have bad influences on workers health.
3.Easy application: The hotmelt adhesive film will be easier to bond the materials, and can save time.
4.It is a product which can be high temperature resistance, a special characteristic.
It is mainly used in the microfiber and EVA chips, fabrics, paper, etc.
This quality can also to kinds of textile idustry and other materials.
Product detail pictures:




Related Product Guide:
H&H hot melt adhesive film: hot melt adhesive film applied at footwear lamination
H&H hot melt adhesive film: the application of hot melt adhesive film
We attempt for excellence, support the customers", hopes to become the top cooperation team and dominator enterprise for staff, suppliers and shoppers, realizes worth share and continual marketing for Ordinary Discount H&H Printing - EVA HOT MELT ADHESIVE FILM – HH, The product will supply to all over the world, such as: Egypt, USA, Washington, we always keep our credit and mutual benefit to our client, insist our high quality service to moving our clients. always welcome the our friends and clients to come and visit our company and guid our business, if you are interested in our products, you can also submit your purchase information online, and we will contact you immediately, we keep our highly sincere cooperation and wish everything in your side are all well.
High production efficiency and good product quality, fast delivery and completed after-sale protection, a right choice, a best choice.